Activated polymer materials and process for making same

ABSTRACT

THIS INVENTION CONCERNS NON-POROUS, POLYMERIC ARTICLES HAVING ACTIVE ANTIBACTERIAL, ANTIFUNGAL AND COMBINATIONS OF ANTIBACTERIAL AND ANTIFUNGAL PROPERTIES. SAID ARTICLE COMPRISES A PREFORMED, SOLID, NON-POROUS, POLYMERIC SUBSTRATE, AND A SOLID NON-POROUS LAYER OF A POLYMERIC COMPOSITION ADHERENTLY APPLIED TO AT LEAST ON SURFACE OF SAID SUBSTRATE, SAID COMPOSITION CONTAINING AT LEAST ONE ACTIVATING AGENT SELECTED FROM THE GROUP CONSISTING OF ANTIBACTERIAL, ANTIFUNGAL, AND COMBINATIONS OF ANTIBACTERIAL AND ANTIFUNGAL ACTIVATING AGENTS. SAID AGENT IS DISTRIBUTED WITHIN SAID POLYMERIC COMPOSITION OF SAID LAYER AND BEING CAPABLE OF MIGRATING FROM SAID LAYER INTO AND THROUGHOUT SAID SUBSTRATE. SAID AGENT IS PRESENT IN SAID LAYER IN SUFFICIENT AMOUNT SO THAT UPON MIGRATION FROM SAID LAYER INTO SAID SUBSTRATE, AN EFFECTIVE LEVEL OF ANTIBACTERIAL, ANTIFUNGAL OR A COMBINATION OF ANTIFUNGAL AND ANTIBACTERIAL ACTIVITY IS PROVIDED THROUGHOUT SAID SUBSTRATE, AND ON AT LEAST ONE OTHER SURFACE OF SAID SUBSTRATE WHICH IS NOT IN DIRECT CONTACT WITH SAID LAYER.

United States Patent US. Cl. 42419 97 Claims ABSTRACT OF THE DISCLOSURE This invention concerns non-porous, polymeric articles having active antibacterial, antifungal and combinations of antibacterial and antifungal properties. Said article comprises a preformed, solid, non-porous, polymeric substrate, and a solid non-porous layer of a polymeric composition adherently applied to at least on surface of said substrate, said composition containing at least one activating agent selected from the group consisting of antibacterial, antifungal, and combinations of antibacterial and antifungal activating agents. Said agent is distributed within said polymeric composition of said layer and being capable of migrating from said layer into and throughout said substrate. Said agent is present in said layer in sufficient amount so that upon migration from said layer into said substrate, an effective level of antibacterial, antifungal or a combination of antifungal and antibacterial activity is provided throughout said substrate, and on at least one other surface of said substrate which is not in direct contact with said layer.

This application is a continuation-in-part of Ser. No. 593,267, filed Nov. 10, 1966, now abandoned.

BACKGROUND OF THE INVENTION (1) Field of the invention The present invention relates to non-porous, natural and synthetic polymeric articles having chemical and/ or physical or other active properties or combinations of properties. The invention also relates to methods for preparing such articles.

More specifically, the invention relates to polymeric articles having active properties and to the manufacture of such articles by applying to a surface of the article selected activating agents which are capable, in migrating or moving throughout the body of the article, of imparting an effective level of activity throughout the article and/or on a surface other than the one to which the activating agents have been applied.

(2) Description of the prior art It is known in the art that active properties can be imparted to polymeric articles by a variety of methods. One common method is to incorporate one or more activating agents into the polymeric compound during the mixing or blending phase prior to processing or manufacturing the article. Activation is accomplished by thoroughly distributing the activating agents throughout the compounding ingredients. For example, synthetic thermoplastics, natural and synthetic rubbers and other polymeric materials have been blended with activating agents such as, antibacterial, antistatic, electrically conductive and other chemically or physically active agents. The activated polymeric materials are then formed into sheets, fibers, rods or other configurations by molding, casting, ex-

3,705,938 Patented Dec. 12, 1972 truding, calendering and/ or other manufacturing or processing operations.

This method has many shortcomings. Often, certain active properties cannot be obtained, as when the pres ence of the activating agents in the polymeric compound causes ditficulties during the processing, shaping and/ or finishing of the article. In calendering, for example, the presence of the active ingredient often makes it difiicult to attain an integral film. Activating agents which decompose or volatilize at the processing temperatures normally required for calendering cannot be incorporated in the pre-mix compound. Also, activating agents producing toxic vapors during processing require expensive manufacturing procedures, controls and equipment.

Another serious shortcoming of this method is that components, such as polymeric film used in laminates, must be produced with the activating agents incorporated in them prior to conversion to the finished article. When similar articles are made from active and inactive components, such as laminates made from active and inactive calendered polymeric film, the films must be kept in stock in both active and inactive grades. If various types of activity are desired, stocks must be maintained having each type of activity, which is an expensive procedure.

A second method widely used to impart certain active properties to the exposed or working surface is to apply a compound containing active agents to that surface. For example, anti-fouling marine paints, anti-fungal sprays and coatings, fire resistant coatings and antistatic coatings have been applied to the surface of the article. The activity of such coatings is superficially skin deep and surface activity is lost to the extent that the activated coating peels or is mechanically abraded, chipped or washed away from the inactive substrate. While this method affords certain flexibility in providing an activated surface, it is at best subject to limitations of available range of active ingredients that can be applied in this mannerplus limited service life and efiiciency.

Another method for the production of activated articles is to expose the article to the vapors of a volatilized chemical. This ancient technique has long been applied to textiles, polymer sheets, or the like and comprises vaporizing a volatile agent, usually a biologically active agent, and then exposing the textile or other article to the vapors. A major disadvantage of this method, however, is that it requires special buildings, ventilation and recovery equipment, and safety procedures. Since the active agent has a volatilization temperature which necessarily is much lower than the melting point of the article to which the activating vapors are applied, the activation may be readily lost where the article is exposed to elevated temperatures. Thus, the treated material may be rapidly deactivated when subjected to wet or dry heat, for example, by exposure to steam sterilization or other high temperature washing procedure, intense sunlight, etc.

An important object of this invention, therefore, is to overcome the disadvantages of the prior art by providing a method for activating non-porous polymeric articles by applying the activating agents to one surface of the article so that the agents migrate throughout the body of the article and impart an effective level of activity throughout the article and on surfaces to which the activating agent has not been applied. The articles made by this method comprise an active layer which is applied on one surface of the article, and which contains an active migrating agent. The concentration of the agent is in excess of the concentration needed to provide an effective level of activity in the layer, and is sufi'icient, upon migration of the agent from the layer, to impart an effective level of activity throughout the entire article. The high concentration of the active migrating agent in the layer 3 also provides a reservoir of activating material capable of replenishing the efiiective surface activity of the article;

The methods and products of this invention do not require extreme processing conditions so that volatile activating agents are conveniently used at normal temperatures; toxic agents can be handled safely; and a wide variety of inactive polymers can be given almost any desired activation. Only stocks of inactive articles are needed and the desired activation may be applied when desired. The activated article has long lasting properties which persist even if a surface layer is removed and which are replenished from the reservoir of activating agent contained Within the active layer.

Disclosures of procedures representative of the prior art known to applicants are to be found in the US. Pats. Nos. 359,166, Mathieu, issued Mar. 8, 1887; 2,272,397, Becher, issued Feb. 10, 1942; 2,770,566, Ritter, issued Nov. 13, 1956; 2,785,106, Mendelsohn, issued Mar. 12, 1957; 2,919,200, Dubin et al., issued Dec. 29, 1959; 2,933,401, Schmitz-Hellebrecht, issued Apr. 19, 1960; 3,096,183, Geuth, issued July 2, 1963; 3,247,058, Hyman, issued Apr. 19, 1966; 3,279,986, Hyman, issued Oct. 18,

1966; 3,288,669, Heckenbleikner, issued Nov, 29, 1966;

and 3,308,488, Schoonman, issued Mar. 14, 1967.

THE INVENTION IN BRIEF This invention generally comprises the production of non-porous, polymeric articles having active properties by applying to the surface of a preformed polymeric article a layer containing a selected activating agent which is capable of migrating through the body of the polymeric article to impart active properties throughout the article and/or on surfaces not contacted by the layer.

Specifically, the present invention concerns the introduction of chemically and physically active properties into a preformed article of non-porous polymeric material. The active properties which are introduced into the polymeric article include, but are not limited to, chemical properties, such as, biological properties, for example, antibacterial, antifungal, odorous, pesticidal, repellent and insecticidal properties, and physical properties, such as, electrically conductive, and antistatic properties, and combinations of such active chemical and physical properties.

DETAILED DESCRIPTION OF THE INVENTION The invention may be applied to any non-porous polymeric article, regardless of the shape or configuration of the article, or the process by which the article is formed.

The activated article may be in any form, for example, single sheets or multi-ply laminates, films, rods, fibers, woven and non-Woven fabrics, etc., and the article may have been produced by any molding, shaping or fabricating method, such as, casting, extrusion, calendering, or any other conventional forming process.

The non-porous, polymeric articles to which the invention may be applied comprise any natural or synthetic material, including any natural or synthetic thermoplastic or thermosetting polymer.

Articles of polymeric materials, used to protect man and his possessions from the environment may be made by the present invention. Activated polymeric articles, whether reinforced, or combined with other materials, are especially suited to production by the present method. Items which can be produced by the present method include protective coverings for equipment, livestock and materials, protective clothing, mattress ticking, hospital hotel, motel, school fabrics, upholstery, wall coverings, curtains, packaging, tubing, floor tiles, fioor coverings, plastic laminated furniture, counter tops, plastic clad metals, liners and coverings for food processing equipment and installations.

The invention is particularly useful in the production of activated polymeric articles in the form of rigid or flexible sheets or films, in single or multi-ply products, including laminate i p ra g g d su str t o flexible sc m or other woven or non-woven reinforcing, backing or facing components.

The activating agents may be applied in solid or liquid form by any suitable procedure. The activating agent may be applied and maintained as a liquid encapsulated between plies of a laminate or may be set or hardened to solid form. The activating agent may be applied as a solid, such as, a preformed layer or as a layer of discrete particles. Depending on the characteristics of the activating agent, it can be conveniently dissolved or dispersed in a solvent or carrier vehicle which is then applied to the surface of the polymeric substrate, or it may be applied directly without a solvent, binder or carrier vehicle, or the like.

More specifically, in many instances it is convenient to apply the active agent as a solution in a volatile solvent; a solution or dispersion in a liquid vehicle composed of a resin binder in an aqueous or other emulsion; a solution or dispersion of the active agent in a solids vehicle; or a solution or dispersion in a combination of vehicles including solutions, emulsions and 100% solids vehicles. The necessary condition is that the active agent be applied in conjunction with a medium through which the agent can effectively migrate to reach the article to be activated.

Any procedure, such as, coating, spraying, dipping, immersion, printing, dusting, or sheet-to-sheet bonding or laminating may be utilized to achieve the necessary contact between the activating agent and the polymeric substrate, so that an effective level of activation may be im parted to the polymeric article. The process does not depend upon specific temperatures, pressures, and contact times, and may be effected under ambient conditions or under elevated temperature and/or pressure, depending on the method employed. Most activating agents impart eifective activity throughout the article within approximately one week. Some activating agents may impart effective activity more quickly, while others may take a somewhat longer period of time to impart an effective level of activity. Many active agents will not perform in accordance with this invention and thus will not impart effective activity, no matter what the length of contact time.

As noted above, the invention may be utilized to produce polymers having chemical activity, including but not limited to biological activities, such as antibacterial, antifungal, pesticidal, insecticidal, animal repellent and odorous properties; and physical activity, including but not limited to antistatic and electrically conductive properties.

One embodiment of the present invention relates to a process for producing biologically active, e.g., antibacterial, polymeric materials and to the resulting products. Specifically, this aspect of the invention relates to antibacterial materials incorporating a body of non-porous polymer, such as, one or more films of plastic.

Various fibers, fabrics and combinations thereof having antibacterial activity are well known. Such products have been widely used in hospitals, laboratories, shops, homes, and in the outdoors as protective covers, mattress and pillow ticking and covers, wall coverings, etc. Most of these articles are often repeatedly subjected to high temperature washing operations and tend to lose their antibacterial activity over the period of use.

This embodiment provides a process for producing antibacterial polymeric articles, such as, plastic sheet materials in which the antibacterial properties are present throughout the entire body of the material, and also provides improved antibacterial plastic sheet or other polymeric materials having superior resistance to loss of activity during washing and laundering.

By Way of illustration, the method of this invention may be practiced in the field of biologically active materials by providing a substrate of a non-porous polymeric article, such as a plastic sheet, and applying to one surface of the sheet a polymeric liquid composition which contains a selected antibacterial agent whi h migrates throughout the body of the plastic sheet and imparts an effective level of antibacterial activity on the surface of the sheet opposite to the surface to which the active polymeric liquid composition has been applied.

This antibacterial activity is effective against bacteria, including both gram positive and gram negative orgamsms.

The active polymeric liquid composition may then be set to form a solid film on the surface of the plastic sheet. As a result, the product exhibits effective antibacterial acactivity on both surfaces and throughout the body of the plastic sheet.

-In an especially preferred embodiment of the invention, an activated polymeric liquid composition is introduced as a core layer between outer plies of flexible sheets of polymeric material, at least one of which is a flexible sheet of non-porous polymeric material. After setting of the polymeric liquid composition as a core layer to form a solid laminated product, the migration of the antibacterial agent from the core through the outer ply of non-porous polymeric material is found to have imparted an effective level of antibacterial activity to the outer surface of the ply.

In the manufacture of laminated materials, as above described, very valuable commercial materials are obtained by using two outer plies of non-porous, polymeric sheet material, such as, flexible polyvinyl chloride sheets or films, and by reinforcing the structure with a textile element between the outer plies to provide an especially tough, durable and abrasion resistant material.

In practicing the invention with respect to single or multi-ply polymer sheet applications, there may be used as the sheet of polymer, any polymeric material which is capable of being formed into a self-supporting continuous sheet or film, having adequate mechanical properties to withstand normal handling, abrasion, etc. The polymeric material in sheet form must be substantially nonporous. Suitable materials include various hydrocarbon polymers, such as, rubber, and olefins, for example, polyethylene and polypropylene, imide, amide, ester, urethane, carbonate, cellulosic, halocarbon, ionomer, vinyl, such as polyvinyl chloride, polyvinylidene chloride, polyvinyl acetate, and other polymers, and their blends, interpolymers and copolymers.

Polyvinyl chloride films are especially useful in the invention. While thickness of the sheet material is not critical, and articles of around 0.100 inch thick can be produced, excellent results have been obtained with single sheets having a thickness of about 0.015 inch, and with multi-ply laminates having a combined thickness of about 0.030 inch.

The polymeric liquid composition which is applied to the surface of the polymer substrate, in accordance with one embodiment of the invention, may include any liquid composition capable of being set to form a solid film of plastic on the surface of the base sheet. Thus, the term should be understood to include plastisols, polymer solutions, polymer-in-liquid emulsions, and 100% solids liquid polymers.

As the antibacterial agent, there may be employed any antibacterial material capable of being carried in the polymeric liquid composition and capable of migrating through the polymer base sheet.

Where a reinforcing element of closely woven, loosely woven or non-woven textile is employed in the production of laminated products, any suitable fiber, such as, cotton, nylon, polyester, fiber glass or other fibers, may be employed.

Where flexible or rigid laminated materials are prepared, the polymeric liquid composition is preferably a plastisol or other adhesive which bonds together outer plies of the non-porous, ploymeric sheets and may also bond the outer plies to rigid substrates, such as wood or metal, or to flexible substrates, such as reinforcing fabrics, for example, a nylon scrim or other textile fabric. Laminates may also be formed by bonding a single ply of the non-porous polymer to a layer of reinforcing material by means of the plastisol adhesive. For example, a particle board or other rigid substrates may be surfaced with a non-porous polymeric film, such as a wood grain printed polyvinylchloride film using an adhesive containing an antibacterial activating agent which migrates through the polymeric film to impart effective antibacterial activity to the outer surfaces. Such products may be used as counter tops or furniture components in hospitals, bathrooms and other areas requiring these properties.

The invention as applied to biologically active products will be more full appreciated in the light of the following examples. In connection with these examples, certain tests were employed to evaluate the effectiveness of the method of the invention in imparting active properties to inactive polymeric article.

DESCRIPTION OF TEST METHODS In the evaluation of the invention relative to antibacterial effectiveness, the following four tests were employed:

(A) NYS-63 antibacterial test method (1) Test bacteria were transferred daily in American Association of Textile Chemists and Colorists (AATCC) Bacteriostasis Broth containing 5% dextrose. A 0.01 ml. sample of a 24 hour broth culture was transferred and incubated at 37 C.

(2) Culture media used in the tests were of the following compositions:

Distilled water, 600 ml.

Dissolve the Lecithin and Tween in 400 ml. of hot distilled water and boil until clear; add Part II and boil ten minutes; adjust the volume to 1,000 ml.; adjust the pH to 7.0+0.2 with N/ 1 NaOH or N/ 1 HCl filter through coarse filter paper, dispense and sterilize at 15 lb. stream pressure for 20 minutes.

(3) The AATCC Agar used in the test was of the following composition:

G. Peptone 10 Sodium chloride 5 Beef extract 5 Agar agar 15 Distilled water, 1000 ml.

(4) The antibacterial test procedure was as follows:

(a) Size of inoculum per sample.-The inoculum should contain suflicient organisms in AATCC bacteriostasis broth. The dilution should be made from a 24 hour both culture in which the number of organisms per unit volume has been accurately and rapidly established by a suitable counting method.

(b) Size and shape of test sample.--Cut one square inch discs from the test material.

(c) Controls.--Samples of control material containing no antibacterial agent shall be inoculated in the same manner as the test samples.

(d) Inoculation of polymer.-Two or three bottom sections of 35 x 10 mm. disposable tissue culture dishes (Falcon catalogue #1008) shall be placed in standard petri dishes containing 10 ml. of sterile distilled water. Place 0.2 ml. of a 24 hour broth culture containing 10 organisms in the center of each disposable tissue culture dish. The test and control discs shall then be placed in the disposable tissue culture dishes with treated surface in contact with inoculum. The covers shall then be replaced on the standard petri dishes. The latter shall be placed on a level shelf in an incubator at 37 C. This procedure provides for optimal growth of the bacteria at 100% relative humidity.

(e) Incubation.Tl1e samples shall be incubated at 37 C. for 24 hours.

(f) Sampling of inoculated swatches.-After incubation for the prescribed periods, the disposable tissue culture dishes containing the sample shall be removed from the petri dish by means of a flamed forceps and placed into 50 ml. of letheen broth in an 8 oz. Wide mouth jar. Shake vigorously for about one minute after sample and tissue culture dish are separated. Make serial dilutions and place in AATCC bacteriostasis agar.

(g) Incubate plates for 24 to 48 hours at 37 C.

(h) Calculate percentage reduction of the inoculum by treated samples vs. untreated samples.

(B) NYS-63 Modified Antibacterial Test-Tripticase Soy Broth is used instead of Letheen Broth.

(C) Agar Plate MethodAATCC Method 90-1965T (D) Modified Agar Plate Method-AATCC Test Method 901965TAppendix A-l-(Seed Layer) With reference to the NYS-63 tests for antibacterial activity, an elfective level of such activity is considered to be one which gives at least 70% reduction in bacteria growth as compared with a control sample.

With respect to the Agar Plate Method and Modified Agar Plate Method tests for antibacterial activity, an effective level of such activity is judged by visual observation of a zone of inhibition of bacteria growth around a specimen. If there is any observable zone of inhibition around the specimen, the level of activity is judged to be elfective.

In connection with the following group of examples in which antibacterial activity is evaluated by the foregoing test methods A-D inclusive, the evaluations were made with reference to the following bacteria:

(a)-- S. Aureus (gram positive) American Type Culture Collection No. 6588. (b)--- E. 0011' (gram negative) American Type Culture (E) Fungistatic Test Method In evaluating effectiveness of the invention to impart fungistatic properties to unactivated polymeric articles, the following test procedure was employed:

(a) Pour Nutrient-salts agar into sterile petri dish and let it solidify. The nutrient salts were prepared as described in ASTM D192463 Test Method.

(b) Place test sample disc, along with a control, on top of agar.

(c) A piece of sterile filter paper, slightly smaller than the petri dish, is then placed over the top of the test sample discs and the whole plate is then sprayed (from a sterile atomizer) with a prepared spore suspension of Chaetomium Globosum', or other fungi spores.

(d) The dish is then covered with a lid and placed in the incubator at 28 C.30 C. Results based on visual observation of inhibition are recorded at 7-day intervals for a total of 2.1 d ys.

(e) Growth above the test disc is compared with growth above the untreated control disc to determine effectiveness.

With reference to the antifungal test method the level of activity is determined by visual observation of the relative inhibition of fungal growth over a specimen, when compared with a control sample. The extent of fungal inhibition was graded as follows: total, high, moderate, low and no inhibition. The level of activity is considered effective where moderate or greater inhibition is observed.

Further, with respect to the following examples, a studied effort was made to demonstrate the eflicacy of the invention as applied to systems comprising all of the common polymeric substrate materials and representatives of the major categories of biologically active chemical compounds. Thus, phenolic, metallo-organic, inorganic metal salt, organic sulfur, antibiotic, quaternary amine, carbonyl, carbocyclic and halogneated carbocy clic, and other biologically active compounds were successfully employed in accordance with the invention.

Not every biologically or otherwise active agent successfully migrates in each polymeric substrate to impart the desired level of activity and a certain amount of selection is required on the part of those practicing this invention. However, operable systems embodying all of the common commercial polymers and the recognized types of biologically active agents or other active agents have been demonstrated and other systems incorporating these and other related material will be seen to be feasible on the basis of this disclosure.

The primary subject matter of the various groups of specific examples may be summarized as follows:

Examples 1-7 and 10-12-Preparation of polyvinyl chloride articles having biological activity Example 13Permanence of activity Examples 8-9 and 1559Prepartion of biologically active articles comprising various combinations of polymeric substrate and biologically active agent Examples 71-73Preparation of textile fibers having biological activity Examples 77-87-Preparation of biologically active articles comprisnig multi-ply polymeric substrates Examples 69-70-Preparation of polymeric articles having odorous properties Examples 74-75-Preparation of polymeric articles having repellant properties Examples -97--Preparation of polymeric articles having antistatic properties In the following examples, the biologically active agents which have been utilized are identified as follows:

Chemical designation Type Dowiclde A o-Phenylphenol sodium salt Phenolic. Metasol 57-. Phenylmercurio proplonate. Metallo-organic. Arquad 8-50- Trlmethyl soyammonium Quaternary chloride. organic salt. Captan N-(trichloromethflthlQ-l- Organic sulfur.

pgclohexene-lJ-dlcarboxtme. TBTSS- Bls(tri-n-butyltin)suliosalicylate. Metallo-organic, organic sulfur. Mercurle chloride Mercury blchlorlda. Inorganic metal salt. Paraformaldehyde lrloxymethylene Carbonyl. Tetracycline HCl- -(dimethyl amino)-l,4,4a, 5, Antibiotic.

5a, 6,11,12a-octa-hydro-3,6,l0, 12.12a-penta-hydroxy-6- methyl-1,ll-dioxo-2-naphthacenecarboxamlde hydrochloride. BloMeT-M Dipheuylstiblne 2-ethyl hexoate Metallo-organlc.

Pyrethrlns Carbocycllc,

carbonyl. Plperonyl butoxldc Synergistic with pyrcthrins. Hexachlorophene. 2,2-methylenebis 3,4,6-tri- Phenolic.

c lorophenol. Hyamlne 1622 Diisobutylphenoxyethoxyethyl Organic salt.

dimethyl benzyl ammonium chloride, mcnohydrate. Hyamlne 3500 n-Alkyl dlmethyl benzyl Quaternary ammonium chloride. organic salt. Metasol BT.. Phenylmec lc b0rate......-. a. etallobrganlc.

Tri-n-butyltin neodecanoate. 10,10'-oxybisphenoxyarsine Metallo-organlc.

Copper-S-quinolinolate. D0. Trl-n-butyltiu linoleate D0. Trl-n-butyltin monopropylene- Do.

glycol maleate. Tri-n-butyltin acetate Do.

EXAMPLE 1 There was provided a sheet of polyvinyl chloride film having a thickness of 0.00375 inch. One surface of the film was then coated with a plastisol coating containing about 3% by weight of the film of tri-n-butyltin neodecanoate as an antibacterial agent. The plastisol was prepared by dispersing 100 parts of polyvinyl chloride resin and about 8 parts of calcium carbonate in about 100 parts of dioctylphthalate and then dispersing 13.5 parts of tri-n-butyltin neodecanoate into 200 parts of plastisol. The plastisol was stirred until uniform and the coating was applied to the base sheet in a thickness of about 0.002 inch.

The antibacterial properties of the resulting product were then determined by the NYS-63 Method.

Control experiments were also performed concurrently and the percent reduction in growth in the presence of the antibacterial agent was observed. The tests of the material produced in accordance with this example showed that the uncoated side of the polyvinyl chloride film gave a 90% reduction in bacterial growth in comparison with the control material.

The coated side of the resulting material gave a 96% reduction in bacterial growth.

The amount of antibacterial agent employed in this and the following examples is suflicient to provide up to about by weight of the combined weight of the inactive polymer layers, after drying of the liquid polymer composition.

EXAMPLE 2 A sheet of polyvinyl chloride film having a thickness of 0.013 inch was coated with a plastisol composition, as described in Example 1, but containing about 3%, based on total polyvinyl chloride film weight, of a solution of 10,10'-oxybisphenoxyarsine in epoxidized soybean oil as the antibacterial agent.

The coated polyvinyl chloride film was then overlayed with a piece of nylon scrim and a second sheet of polyvinyl chloride film, this one haiving a thickness of 0.00375 inch. The laminate was allowed to set under suitable conditions of heat and pressure until an integral, firmly bonded product was obtained.

Upon testing by the NYS-73 Method, it was found that the outer surface of 0.013 inch thick polyvinyl chloride film gave a 99.6% reduction and the outer surface of the 0.00375 inch polyvinyl chloride film a 99.7% reduction in bacterial growth when tested against S. Aureus, as compared with a control sample.

EXAMPLE 3 A fabric was prepared by coating a 0.00375 inch polyvinyl chloride film with a plastisol containing 100 parts polyvinyl chloride, 50 parts Kodaflex AD2, a polymeric plasticizer, dioctylphthalate, Texanol isobutyrate, epoxidized soybean oil and a heat stabilizer and about 3% of the same antibacterial agent used in Example 2. The coated base sheet was then overlayed with a nylon scrim element and a sheet of 0.00375 inch polyvinyl chloride, and was allowed to set under suitable conditions of heat and pressure until an integral, firmly bonded product was obtained.

The resulting fabric evidenced a 99.4% reduction in bacterial growth on one outer surface and a 99.5% reduction on the other, as compared with a control sample.

EXAMPLE 4 Two 0.00375 inch polyvinyl chloride film elements were laminated to a nylon reinforcing element by means of the same plastisol composition and conditions as was used in Examples 1 and 2, except that no antibacterial agent was present in the plastisol. This control experiment showed only a 42% reduction in bacterial growth on one side of the product and 0% reduction on the opposite side.

EXAMPLE 5 A 0.00375 inch thick sheet of polyvinyl chloride film was coated with a water-based emulsion of polyvinyl chloride, Geon 576, containing about 1.5% by weight of copper-8-quinolinolate based on the weight of Geon 576. The film of the polymer was drawn down on the vinyl film and then dried.

Upon testing, the product showed a 95.5% reduction in bacterial growth on the untreated side, as compared with a control sample.

EXAMPLE 6 A 0.00375 inch thick polyvinyl chloride base sheet was coated with a solids liquid polymer system consisting of Epon 828-triethylene-tetramine which is cured in the presence of about 5% of the antibacterial solu tion used in Example 2, based on the total weight of the laminate. A nylon scrim element was applied as a backing to the polyvinyl chloride base sheet. The liquid polymer system contains no solvent or Water as a carrier. A 98.5% reduction in bacterial growth was observed on the outer side of the polyvinyl chloride base sheet and a 98.6% reduction was observed on the nylon scrim side of the product.

EXAMPLE 7 The same material was prepared as in the preceding example except that the antibacterial agent was omitted. A 0% reduction in bacterial growth was observed on both sides.

EXAMPLE 8 A sheet of Aclar, a fiuoro halocarbon film, and having a thickness of 0.001 inch, was coated with the plastisol composition of Example 1 containing about 5% of the antibacterial solution of Example 2, based upon film weight. After setting of the plastisol, the material was tested and showed an 84% reduction in bacterial growth on the outer side of the Aclar sheet. A 98% reduction in bacterial growth was observed on the plastisol coated side.

EXAMPLE 9 Material was prepared in the same manner as in the preceding example, except that the antibacterial agent was omitted. A 0% reduction in bacterial growth was observed on the outer side or surface of the Aclar base sheet and only a 10% reduction was observed on the plastisol side.

EXAMPLE 10 A laminated fabric was prepared under the conditions of Example 1 from two sheets of 0.00375 inch polyvinyl chloride film and a woven nylon scrim element using the plastisol of Example 1 as an adhesive, except that 22 parts of tri-butyltin linoleate to 100 parts of plastisol was used as the antibacterial agent. Sufiicient plastisol was used to apply about 5% of antibacterial agent based on film Weight. An average bacterial growth reduction of 89% is observed on the surfaces of the laminate, when compared with a control sample.

1 1 EXAMPLE 11 Material was prepared as in Example 10, except that 13 parts of the same antibacterial solution as was used in Example 2 were employed as the antibacterial agent and the concentration of antibacterial agent was bout 3% based on the film weight. An average reduction in bacterial growth of 99% is observed on the surfaces of the laminate, when compared with a control sample.

EXAMPLE 12 An antibacterial material was prepared as in Example 10, except that 2.3 parts of tributyltin monopropylene glycol maleate is employed as the antibacterial agent and the concentration of antibacterial agent was about 0.5% based on the film weight. An average reduction in bacterial growth of 96% is observed on the surfaces of the laminate when compared with a control sample.

EXAMPLE 13 The same material was prepared as in Example 10, except that a combination of 13 parts of the antibacterial solution as was used in Example 2 (about 3% based on film weight) and 2.3 parts of tributyltin sulfosalicylate (about 0.5% based on film weight) are employed as the antibacterial agent. An average reduction in bacterial growth of 99% is observed on the surfaces of the laminate when compared with a control sample.

Samples obtained in this experiment were subjected to wash cycles in a Kenmore Electric washer and to autoclave treatment. Each washing machine cycle involved a ten minute wash and three minute rinse, with the wash temperature being 135:5 R, and the rinse temperature being 130:10" F. The autoclave treatment was at 222:6" F. for three hours at a pressure of 1-5 p.s.i. During the washing cycle, cup of Ivory Snow was used for each seventeen gallons of water (full capacity). Sufiicient specimens for testing were removed after various cycles and the wash/rinse/autoclave cycle treatment was repeated. Samples were tested for reduction in bacterial growth after the following treatment and compared to unwashed samples:

Wash cycles: Autoclave cycles The average reduction in bacterial growth remained essentially at 80% of the initial value after 25 wash cycles and six autoclaves.

It is apparent, therefore, that the process and materials of the invention provide an antibacterial eifect in fabrics which persists, substantially unimpaired, through repeated wash and autoclaving treatments.

Other chemical and biological activities, such as, pesticidal, and odorous properties may be introduced into polymeric articles in accordance with the present technique.

It will also be apparent from the following series of examples that combinations of antibacterial agents may be selected to impart effective antibacterial activity against a number of different species of organisms. Likewise, it is demonstrated that a single biological agent or combination of such agents may be selected to provide a polymeric article having a combination of antibacterial, antifungal and other activities, such as, pesticidal, repellent, and odorous activities. In an additional important em bodiment of the invention, combinations of chemical and physical properties may be imparted to polymeric articles in accordance with the invention. For example, antibacterial, antifungal, odorous and antistatic properties may all be combined in a polymeric substrate, such as, single or multi-ply fabrics to provide highly desirable products 12 for use in hospitals or other environment where such a combination of properties is very advantageous.

EXAMPLES 14 TO 59 In the following series of examples, a wide variety of common, commercially available polymer materials were treated in accordance with the invention to impart chemical activity. Special emphasis was placed on the selection of polymers of widely different chemical types to demonstrate the general application of the invention to nonporous polymer substrates. Commercially available species of most of the prominent commercial types of polymers were utilized and found to be satisfactory for the practice of this invention in combination with selected activating agents.

Likewise, a studied effort was made in the following examples to demonstrate the efiicacy of this invention when applied to a wide variety of different types of commercially available biologically active agents. Thus, phenolic, metallo-organic, inorganic metal salt, organic sulfur, antibiotic, quaternary amine, carbonyl, carbocyclic and halogenated carbocyclic, and other biologically active compounds were successfully employed in accordance with the invention.

In the following series of examples, the invention was applied to a wide variety of polymer sheet materials of varying construction. The different types of sheet and laminate constructions used in these examples are designated in Table 1.

activating agent. C Cloth/film containing activating agent/cloth.

D Film/plastisol containing activating agent/nylon/film. E. Film/solid activating agent (no binder or solvent) lfilm. F. Film/liquid activating agent (no hinder or solvent)! G Film/film (inactive system).

H Film/plastisol/nylon scrim/film (inactive system).

I Film/plastisol containing activating agent.

rubber in VMdzP Name Chemical Description Aclar Polychlorotrifluoroethylene. Tedlar Polyvinyl fluoride. Tuftane Polyester urethane. Kapton Polybenzimidazole. Surlyn A Partially neutralized copolymer of ethylene and ionomer resin. Mylar Polyethylene terephthalate. Saran Polyvinylidene chloride.

acrylic acid- Antibacterial test Bacterial Percent Antifungal species reduction inhibition TAB LE 2 Nominal percent active Construction code coating Inactive film agent based solution No. and subthickness on total strate polymer (inches) weight Biological agent Example number 1 Quantitative analysis of pesticide was performed colorimetrically.

The latex utilized was Hycar-ISSZ and the pesticide EXAMPLES 69-70 The invention also showed utility in the production of non-porous, polymeric articles having active odorous propwas Pyronyl 101, an emulsion concentrate of 1.2% pyrethrins and 12.0% piperonyl butoxide. The laminates were tested with corn meal with the polymer film side of the laminate facing the grain After two weeks, the com 75 erties, as shown in the following examples.

EXAMPLE 69 A laminate of two 0.004 inch thick films of polyvinyl chloride was formed incorporating a nylon scrim reinforcing element and using a plastisol adhesive incorporating 0.5% by weight of the laminate of a synthetic leather essence. Immediately after the laminate was formed, it was confirmed by a smell test of the resulting product that a distinct leatherdike odor had been imparted to the product.

EXAMPLE 70 Example 69 was repeated except for the substitution of a synthetic rose essence for the leather essence and the use of 0.00875 and 0.0055 inch thick plies of polyvinyl chloride. Immediately after the laminate was formed, the smell test confirmed the presence of a distinct rose-like odor emanating from the outer surface of the laminate.

EXAMPLES 71-73 One of the preferred embodiments of this invention includes the use of a textile fabric which has been activated by contact with an active layer by migration of the active ingredient into the body of the fibers of the cloth. This eifect is independent of the porosity of the fabric, and in fact is not related to the porosity. It has been shown in the prior art that porous substrates may be activated by means of an adhesive containing an active agent introduced between layers of porous material. Examples 71 through 73 demonstrate that it is not necessary that porosity exist in a textile fabric, since, according to this invention, the yarns or fibers themselves may be made to take up the active agent by migration. The advantage of this is that the active ingredient is not easily washed out by laundering, but becomes an integral part of the substrate yarns. As with other products of this invention, active properties on the surfaces of the fibers are continuously replenished from the reservoir of active agent within the active layer.

EXAMPLE 71 A fabric was prepared by placing a cotton woven cloth having a thickness of about 0.015 inch in contact with an active film of polyvinyl chloride containing the antibacterial agent, captan. The captan was present in an amount to provide 0.53% of the active agent based on the total weight of the composite.

The side of the cloth not in contact with the active film was then tested by the modified Agar Plate Method for antibacterial activity against S. Aureus. The uncontacted side of the cotton cloth exhibited an elfective level of antibacterial activity as it was observed to provide a 2.75 mm. zone of inhibition.

EXAMPLE 72 A sample was prepared by placing a completely desized cotton textile, 0.012 inch thick, against an active film 0.0055 inch thick and containing 3.0% of Metasol BT, based on the total weight of the laminate, under a pressure of 3.3 p.s.i. for 96 hours and allowing the active agent to migrate into the fibers of the textile. The textile was then separated from the active film and the side which had been out of contact with the active film was tested by the NYS- 63 Method for activity against S. Aareus. A 99.9% reduction in bacterial growth was observed.

EXAMPLE 73 A 1%" circle of completely desized cotton fabric was coated around its periphery with a plastisol containing 3.0% of Metasol BT based on the total weight of the sample. The plastisol was hardened by fusing for five minutes at 350 F. and cooling. After 96 hours, at room temperature, only the uncoated center of the disc of cotton fabric was cut out and tested for activity against S. Aurems by the NYS-63 Method. A 99.9% reduction in bacterial growth was observed.

16 EXAMPLES 74-75 The application of the invention in the production of polymeric articles having active insecticidal or animal repellent properties is demonstrated in the following examples.

EXAMPLE 74 A laminate of construction B, incorporating a Saran film 0.00075 inch thick, and coating No. 2 containing 1.8% of Chlordane was observed by scanning electron microscopy. Efiective migration was evidenced by the presence of crystals of. the active agent, Chlordane, on the uncoated surface of the material.

EXAMPLE 75 A laminate of construction B, incorporating a Mylar film 0.00075 inch thick and coating No. 3 containing 2.2% of methyl nonyl ketone was tested as in Example 74 and gave positive evidence of effective migration of the active agent.

Other examples of the application of the invention to the production of antibacterial materials are set forth below.

EXAMPLE 76 (A) A first, integral multi-ply material was produced by laminating together two plies of polyvinyl chloride incorporating 0.4% (by weight based upon the total weight of the laminate) of the active antibacterial agent bis(tri-n-butyltin)sulfosalicylate (the antibacterial agent disclosed in US. Pat. 3,279,986). A layer of plastisol adhesive was employed to assist the bonding of the plies, and a nylon reinforcing fabric or scrim was introduced as a core layer and was sandwiched between the polyvinyl chloride plies.

In this example, surfaces of the laminate were tested for antibacterial activity against S. Aureus.

The outer surface of one of the outer plies of polyvinyl chloride was tested for antibacterial activity by the Agar Plate Method and showed a 0.2 mm. zone of inhibition.

The surfaces of a discrete, untreated film of polyvinyl chloride were then tested for antibacterial activity by the same method and showed no antibacterial activity, i.e., no zone inhibition.

The discrete, untreated film of polyvinyl chloride was then laminated to the previously tested outer surface of one of the polyvinyl chloride plies of the first laminate to form a second laminated product. The second laminate was then tested to determine antibacterial activity on the outer surface of the untreated polyvinyl chloride film, but no activity, i.e., no zone inhibition was found.

(B) The above procedure (A) was followed except for the following variations:

(1) The polyvinyl chloride plies of the first laminate contain no antibacterial agent;

(2) The plastisol had incorporated therein 0.3% (by weight, based upon the total weight of the laminate) of the active antibacterial agent N-[(trichloromethyl)thio]- 4-cyclohexene-l,Z-dicarboxamide.

'One of the outer surfaces of the first laminate was tested for antibacterial activity and showed a 4.8 mm. zone of inhibition. The discrete, untreated film again showed no zone of inhibition prior to lamination.

Upon lamination of the untreated polyvinyl chloride to form the second laminate, however, the outer surface of the untreated film showed antibacterial activity by a 3.5 mm. zone of inhibition.

The foregoing example demonstrates that the phenomenon of this invention is not inherent in the lamination of one polymer film to a pretreated polymer film, but depends upon the proper selection and combination of polymers and active agents.

17 EXAMPLES 77-87 An integral multi-ply material was formed of two plies of polyvinyl chloride containing no antibacterial agent, a plastisol adhesive layer containing an amount and type of antibacterial agent as set forth in Table 4 below and a nylon reinforcing core layer.

Table 4 sets forth the identity and amount of antibacterial agent present in the plastisol adhesive layer (in percent by weight, based upon the total weight of the laminate) and the results of testing for antibacterial activity of the outer surfaces against S. Aureus. The test or antibacterial activity employed is the NYS63 Method.

EXAMPLES 88-89 Examples were prepared according to construction I using 0.004 inch thick polyvinyl chloride film and TBTSS as the activating agent in the plastisol. The samples were tested for antibacterial activity on the uncoated side against S. Aureus using the NYS-63 Method. The results are reported in Table 4.

TABLE 4 Concentration, Percent reducpereent tion of bacteria Ex. based on No. Antibacterial agent film weight Side 1 Side 2 77 N 44.2 50.6 78 Tributyltin neodeeanoate 5. 9S. 0 95. 4 79 Tributyltin linoleate- 5. 0 92. 4 87. 7 80 10,10-oxybisphenoxyarsi 5. O 99. 2 99. 9 81 Tributyltin neodecanoate 0.5 60. 3 55. 1 82 Tributyltin linoleate 0. 60. 2 52. 8 83 Tributyltin monopropylene- 0. 5 95. 6 95. 9

glycol maleate. 10,10-oxybisphenoxyarsine 0. 5 99. 2 99. 6 Tributyltin acetate 0.5 0 32. 9 10,10-oxybisphenoxyarsi 3. 0 99. 9 99. 7 BT S 0.5 49. 4 38. 1 88 TBTSS 0.5 59 TB'ISS 5. 0 26 EXAMPLES 90-97 In another important embodiment, special physical properties may be imparted to polymeric articles in ac cordance with the invention. For example, antistatic and electrically conductive properties may be incorporated into a polymeric article by the present method.

Applications of the invention to impart physical activity to polymeric materials are set forth in the examples which are reported in Table 5. In the examples, Volume Resistivity was tested by Test Method NFPA No. 5 6A, para- 2541 and 254336), and Surface Resistivity was tested by Test Method NFPA No. 56A, para. 25433(3) [AATCC 76-59 Method]. The foregoing are used to determine the electrical conductivity of the tested materials. Antistatic materials have a sufficiently high electrical conductivity to dissipate electrostatic charges which may be generated on their surfaces.

that no active layer was used. The electrical conductivity of each laminate was measured after 48 hours at room temperature. The volume resistivity of the first laminate, containing the active agent, was 5.5 x10 ohms, and of the second laminate, with no activating agent, was 35x10 ohms. The plies of the first laminate were subsequently separated and the activating agent was completely washed off. The plies were recombined as before, but without activating agent, and the volume resistivity was measured and found to be 5.0 10 ohms.

EXAMPLE 99 Two layers of fiber glass fabric, Style 181/ 150, Volan, were impregnated with a fire resistant unsaturated thermosetting polyester compound and combined and hardened with an organic peroxide under heat and pressure to a total thickness of 0.017 inch. A plastisol composition containing Metasol BT at a concentration of 3% by weight of the final laminate was applied to one surface of the polyester/fiber glass layer and hardened at 300 F. for four minutes. The unactivated surface was tested by the NYS-63 Method and effective inhibition of S. Aureus bacteria was observed.

In an additional important embodiment of the invention, combinations of chemical and physical properties may be imparted to polymeric articles in accordance with the invention. For example, antibacterial, antifungal, odorous and antistatic properties may all be combined in a polymeric substrate, such as, single or multi-ply fabrics to provide highly desirable products for use in hospitals or other environment Where such a combination of properties is extremely important. For example, a very useful laminate is provided by bonding two outer plies of 0.004 and 0.00375 inch polyvinyl chloride film to a nylon scrim reinforcing core element by use of a plastisol adhesive containing both Captan and Advastat 50 to impart a combination of antibacterial and antistatic properties to the outer surfaces of the product.

What is claimed is:

1. -A polymeric article having active properties selected from the group consisting of antibacterial, antifungal and combinations thereof comprising:

a solid, non-porous, polymeric substrate, and

a solid, non-porous layer of a polymeric composition adherently applied to at least one surface of said substrate, said composition containing at least one activating agent, selected from the group consisting of anti-bacterial, antifungal and combinations of antibacterial and antifungal activating agents, said agent being distributed within said polymeric composition and being capable of migrating from said layer into and throughout said substrate, said agent being present in said layer in sufficient amount so that upon migration from said layer into said substrate an effec- TABLE 5 Nominal percent Surface Construction code coating active agent Volume resistivity, Example solution No. and sub- Film thickbased on Antistatic resistivity ohms/ number strate polymer ness (inches) total weight agent ohms) square H Polyvinyl chloride 0. 004/0. 0034 None None 91-. D do 0. 004/0. 0034 1.0 Advastat 50- 92" D d0 0. 004/0. 0034 1. 2 Aston 123- 93. G do 0. 0034/0. 0034 None None 04.- F do 0. 0034/0. 0034 11. 2 Advastat 50- 95.--- A do 0. 0034/0. 0034 3.0 do 96 H do 0. 00375/0. 00375 None None 97 D d0 0. 00375/0. 00375 9.6 Naiton-AT EXAMPLE 98 tive level of antibacterial, antifungal or a combination of antibacterial and antifungal activity is provided throughout said substrate, and on at least one other surface of said substrate which is not in direct contact with said layer.

2. A polymeric article having active antibacterial properties comprising:

a solid, non-porous, polymeric substrate, and

a solid, non-porous layer of a polymeric composition adherently applied to at least one surface of said substrate, said composition containing at least one antibacterially activating agent distributed within said polymeric composition and capable of migrating from said layer into and throughout said substrate, and said agent being present in said layer in sufiicient amount so that upon migration from said layer into said substrate an eifective level of antibacterial activity is provided throughout said substrate, and on at least one other surface of said substrate which is not in direct contact with said layer.

3. The article of claim 2 wherein the amount of antibacterially activating agent in said layer is in excess of the amount needed to provide an initial eflfective level of antibacterial activity throughout said article, said excess amount of said agent providing a reservoir of said agent in said layer for the maintenance of an effective level of antibacterial activity in said article by replenishment of said agent from said reservoir.

4. The article of claim 2 wherein said activating agent comprises a phenolic compound.

5. The article of claim 2 wherein said activating agent comprises a metallo-organic compound.

6. The article of claim 2 wherein said activating agent comprises an inorganic metal salt compound.

7. The article of claim 2 wherein said activating agent comprises an organic sulfur compound.

8. The article of claim 2 wherein said activating agent comprises an antibiotic material.

9. The article of claim 2 wherein said activating agent comprises a quaternary organic salt compound.

10. The article of claim 2 wherein said activating agent comprises a carbonyl compound.

11. The article of claim 2 wherein said activating agent comprises a carbocyclic compound having a carbonyl group.

12. The article of claim 2 wherein said activating agent comprises a halogenated carbocyclic compound.

13. The article of claim 2 wherein said activating agent is the sodium salt of o-phenyl phenol.

14. The article of claim 2 wherein said activating agent is phenyl mercuric propionate.

15. The article of claim 2 wherein said activating agent is trimethyl soyammonium chloride.

16. The article of claim 2 wherein said activating agent is mercury bichloride.

17. The article of claim 2 wherein said activating agent is trioxymethylene.

18. The article of claim 2 wherein said activating agent is tetracycline-HCI.

19. The article of claim 2 wherein said activating agent is diphenylstilbine Z-ethyl hexoate.

20. The article of claim 2 wherein said activating agent is hexachlorophene.

21. The article of claim 2 wherein said activating agent. is diisobutylphenoxyethoxyethyl dimethyl benzyl ammonium chloride, monohydrate.

22. The article of claim 2 wherein said activating agent is n-alkyl dimethyl benzyl ammonium chloride.

23. The article of claim 2 wherein said activating agent is phenylmercuric borate.

24. The article of claim 2 wherein said activating agent is 1,2,4,5,6,7,8,8 octachloro 3a,4,7,7a tetrahydro-4,7- methanoindan.

25. The article of claim 2 wherein said activating agent is tributyltin neodecanoate.

26. The article of claim 2 wherein said activating agent is tri-n-butyltin linoleate.

27. The article of claim 2 wherein said activating agent is 10,l-oxybisphenoxyarsine.

28. The article of claim 2 wherein said activating agent is tributyltin monopropyleneglycol maleate.

29. The article of claim 2 wherein said activating agent is copper-S-quinolinolate.

37. The article of claim 2 wherein said substrate comprises polyvinyl fluoride.

38. The article of claim 2 wherein said substrate comprises polychlorotrifiuoroethylene.

39. The article of claim 2 wherein said substrate comprises polyester urethane.

40. The article of claim 2 wherein said substrate comprises polycarbonate.

41. The article of claim 2 wherein said substrate comprises polyethylene terephthalate.

42. The article of claim 2 wherein said substrate comprises polyvinylidene chloride.

43. The article of claim 2 wherein said substrate comprises polybenzimidazole.

44. The article of claim 2 wherein said substrate comprises ethylene-acrylic acid copolymer ionomer.

45. The article of claim 2 wherein said substrate comprises cellulose acetate.

46. The article of claim 2 wherein said substrate comprises regenerated cellulose.

47. The article of claim 2 wherein said substrate comprises a polyamide.

48. The article of claim 2 wherein said layer comprises a plastic film bonded to said substrate.

49. The article of claim 2 wherein said layer comprises an adherent coating of an adhesive composition on said substrate.

50. The article of claim 2 wherein said substrate is a flexible film of polymeric material.

51. A polymeric article having active antifungal properties comprising:

a solid, nonporous, polymeric substrate, and

a solid, non-porous layer of a polymeric composition adherently applied to at least one surface of said substrate, said composition containing at least one antifungally activating agent distributed within said polymeric composition and capable of migrating from said layer into and throughout said substrate, and said agent being present in said layer in suflicient amount so that upon migration from said layer into said substrate an effective level of antifungal activity is provided throughout said substrate, and on at least one other surface of said substrate which is not in direct contact with said layer.

52. The article of claim 51 wherein the amount of antifun-gally activating agent in said layer is in excess of the amount needed to provide an initial effective level of antifnngal activity throughout said article, said excess amount of said agent providing a reservoir of said agent in said layer for the maintenance of an effective level of antifungal activity in said article by replenishment of said agent from said reservoir.

53. The article of claim 51 wherein said activating agent comprises a phenolic compound.

54. The article of claim 51 wherein said activating agent comprises a metallo-organic compound.

55. The article of claim 51 wherein said activating agent comprises an inorganic metal salt compound.

56. The article of claim 51 wherein said activating agent comprises an organic sulfur compound.

57. The article of claim 51 wherein said activating agent comprises 'an antibiotic material.

58. The article of claim 51 wherein said activating agent comprises a quaternary organic salt compound.

59. The article of claim 51 wherein said activating agent comprises a carbonyl compound.

60. The article of claim 51 wherein said activating agent comprises a carbocyclic compound having a carbonyl group.

61. The article of claim 51 wherein said activating agent comprises a halogenated carbocyclic compound.

62. The article of claim 51 wherein said activating agent is the sodium salt of o-phenyl phenol.

63. The article of claim 51 wherein said agent is phenyl mercuric propionate.

64. The article of claim 51 wherein said agent is mercury bichloride.

65. The article of claim 51 wherein said agent is hexachlorophene.

66. The article of claim 51 wherein said agent is phenylmercuric borate.

67. The article of claim 51 wherein said activating agent is l,2,4,5,6,7,8,8-octachloro-3a,4,7,7a-tetrahydro- 4,7-methanoindan.

68. The article of claim 51 wherein said activating agent is tributyltin neodecanate.

69. The article of claim 51 wherein said substrate is a film of solid, non-porous, polymeric material.

70. The article of claim 51 wherein said substrate comprises a hydrocarbon polymer.

71. The article of claim 51 wherein said substrate comprises a polyolefin.

72. The article of claim 51 wherein said substrate comprises polyethylene.

73. The article of claim 51 wherein said substrate comprises polypropylene 74. The article of claim 51 wherein said substrate comprises polyvinyl chloride.

75. The article of claim 51 wherein said substrate comprises polyvinyl fluoride.

76. The article of claim 51 wherein said substrate comprises polychlorotrifluoroethylene.

77. The article of claim 51 wherein said substrate comprises polyester urethane.

78. The article of claim 51 wherein said substrate comprises polycarbonate.

79. The article of claim 51 wherein said substrate comprises polyethylene terephthalate.

80. The article of claim 51 wherein said substrate comprises polyvinylidene chloride.

81. The article of claim 51 wherein said substrate comprises polybenzimidazole.

82. The article of claim 51 wherein said substrate comprises ethylene-acrylic acid copolymer ionomer.

83. The article of claim 51 wherein said substrate comprises cellulose acetate.

84. The article of claim 51 wherein said substrate comprises regenerated cellulose.

85. The article of claim 51 wherein said substrate comprises a polyamide.

86.'The article of claim 51 wherein said layer comprises a plastic film bonded to said substrate.

87. The article of claim 51 wherein said layer comprises an adherent coating of an adhesive composition on said substrate.

88. The article of claim 51 wherein said substrate is a flexible film of polymeric material.

89. The article of claim 51 wherein said substrate is a multilayer laminated material.

90. A polymeric article having a combination of active antibacterial and antifungal properties comprising:

a -solid, non-porous, polymeric substrate, and

activating activating activating activating 22 a solid, non-porous layer of a polymeric composition adherently applied to at least one surface of said substrate, said composition containing at least one antibacterially activating agent and at least one antifungally activating agent distributed Within said polymeric composition and capable of migrating from said layer into and throughout said substrate, said agents being present in said layer in sufiicient amount so that upon migration from said layer into said substrate effective levels of antibacterial and antifungal activity are provided throughout said substrate, and on at least one other surface of said substrate which is not in direct contact with said layer.

91. The article of claim wherein the amounts of antibacterially and antifungally activating agents in said layer are in excess of the amounts needed to provide initial eflective levels of antibacterial and antifungal activity throughout said article, said excess amounts of said agents providing reservoirs of said agents in said layer for the maintenance of effective levels of antibacterial and antifungal activity in said article by replenishment of said agent from said reservoir.

92. The article of claim 90 wherein said antibacterial and antifungal activating agents each comprises at least one material selected from the group consisting of phenolic, metallo-organic, inorganic metal salt, organic sulfur,

' antibiotic, quaternary organic salt, carbonyl, carbocyclic compounds having a carbonyl group, and halogenated carbocyclic compounds.

93. The article of claim 90 wherein said substrate is a material selected from the group consisting of a lower polyolefin, polyvinyl chloride, polyvinyl fluoride, polychlorotrifiuoroethylene, polyester urethane, polycarbonate, polyethylene terephthalate, polyvinylidene chloride, polybenzamidazole, ethylene-acrylic acid copolymer ionomer, cellulose acetate, regenerated cellulose, polyamide and cotton.

94. The article of claim 90 wherein a second material is bonded to said layer.

95. The article of claim 94 wherein said second material is selected from the group consisting of metal, wood, plastic, particle board, paper, textile, asbestos, multilayer laminated elements and elements which serve as a barrier to said activating agents.

96. The article of claim 90 wherein said substrate is a multilayer laminated element.

97. The article of claim 1 further comprising a second material bonded to said layer which contains said activatmg agent.

References Cited UNITED STATES PATENTS 3,578,545 5/1971 Carson et al 16186 3,365,728 1/1968 Edwards et a1 424-183 X 3,345,341 10/1967 Berry et al 42427 X 3,330,729 7/1967 Johnson 42419 3,306,955 2/1967 Lowes 42427 X 3,295,246 1/ 1967 Landsman et al 42427 X 3,279,996 10/ 1966 Long et al 42427 X 3,269,900 8/ 1966 Rubin 42419 3,247,066 4/1966 Milosovich 42419 X 3,034,957 5/1962 Smith et al. 42427 3,279,986 10/ 1966 Hyman 42427 X ROBERT F. BURNETT, Primary Examiner J. C. GIL, Assistant Examiner US. Cl. X.R.

Disclaimer and Dedication 3,7 O5,938.Se3 m0w" H g man, New York, N.Y., Bmce S. Bewwstez'n, Somerville, N.J., and Ramesh Kapooa, Scaford, Del. ACTIVATED POLYMER MATERIALS AND PROCESS FOR MAKING SAME. Patent dated Dec. 12, 1972. Disclaimer and dedication filed Sept. 10, 1973, by the assignee,He1"cuZite Protective Fabrics Ompomtz'on.

Hereby disclaims and dedicates claims 24, 30 and 67 of said patent.